We propose this metal :
Trading : round bars in all diameters
Forge : rings, blocks, bars, rolls (rough or pre-machined pieces, or machined at your sizes).
Carlier designationNc15Fe
UNS designationN06600
European numbering designation2.4816
AFNOR designationNiCr15Fe
British Standard designation3076 (NA14)
Thyssen Krupp VDM designationNicrofer 7216
Aubert & Duval designationAdnic 275E
NACE designationMR0175

Applicable standards
ASTM B166 Bars
ASTM B169 Plates
ASTM B564 Forged pieces

Chemical composition
en %NiCrFeCuMnSSiC
min72 14 -----
max-17 10 0,5 0,015 0,5 0,15 
Density : 8.42


Guarantee mechanical results in MPa
StandardRmRp
0.2%
A %ZHBHrcComments
ASTM B166 - 97a 825 620 Cold rolled rounds, under 12.7 mm 
ASTM B166 - 97a 760 585 10 Cold rolled rounds, from 12.7 to 25.4 mm (incl.) 
ASTM B166 - 97a 725 550 12 Cold rolled rounds, from 25.4 to 63.5 mm (incl.) 
ASTM B166 - 97a 655 310 20 Hot rolled rounds, from 6.4 to 12.7 mm (incl.) 
ASTM B166 - 97a 620 275 25 Hot rolled rounds, from 12.7 to 76.2 (incl.) 
ASTM B166 - 97a 585 240 30 Hot rolled rounds, over 76.2 mm 
ASTM B166 - 97a 585 240 20 Hot or cold rolled and annealed rounds 
ASTM B564 - 97a 552 241 30 Forged metal, and annealed. 

Forging conditions
Forging is made at a range of temperature included between 1150 and 950░C, then cooled at appropriate conditions for the final thermal treatment and obtain required characteristics. In any case, please contact us.

Properties / Main use conditions
This Ni-Cr-Fe alloy has a good strength in caustic atmosphere. It has also a good strength in pure water corrosion. When hardenned, it can be used till a temperature of about 900░C, and has a good resistance to oxidation.

Main applications
Parts for nuclear reactors, transformation from uranium oxids to hexafluoride, production of caustic alkali, of organical or mineral fluorous or chlorunated compounds. Regenerators of catalizators for petrochemical production. Components for industrial ovens. Sparkling electrodes. Equipment for food products treatment.

Heat treatment
Please, contact us