We have not this metal on permanent stock. But we can supply it with a longer delivery time, in any needed shape.
Carlier designationNCK19DTA
UNS designationN07041
European numbering designation2.4973
AFNOR designationNiCr20Co11Mo10TiAl
Aubert & Duval designationPER 41
NACE designation:

Applicable standards
AMS 5712 Bars

Chemical composition
en %NiCrTiAlCoFeMnSSiCBMo
min-18,000 3,000 1,400 10,000 -----0,003 9,000 
maxSolde 20,000 3,300 1,800 12,000 5,000 0,100 0,015 0,500 0,120 0,010 10,500 
Density : 8.4


Guarantee mechanical results in MPa
StandardRmRp
0.2%
A %ZHBHrcComments
AMS 5712 1415 1050 19 All diameters, results with 1 type treatment 
AMS 5712 1100 785 17 All diameters, results with 2 type treatment 

Forging conditions
Forging is made at a range of temperature included between 1150 and 950░C, then cooled at appropriate conditions for the final thermal treatment and obtain required characteristics. In any case, please contact us.

Properties / Main use conditions
Precipitation hardening treatment alloy, with high mechanical properties in the range of temperatures between 870 and 980░C.

Main applications
Warm areas of engines, gas turbines, tools for extrusion.

Heat treatment
1 TYPE :1065░C during 4 hours, air cool, then 760░C during 16 hours, air cool.
2 TYPE: 1175░C during 2 hours, air cool, then 900░C during 4 hours, air cool.