201
|  |
|
|
We propose this metal :
Trading : round bars in all diameters
Forge : rings, blocks, bars, rolls (rough or pre-machined pieces, or machined at your sizes).
|
| Carlier designation | Ni.02 |
| UNS designation | N02201 |
| European numbering designation | 2.4068 |
| AFNOR designation | LC-Ni 99 |
| British Standard designation | 3076 (NA12) |
| Thyssen Krupp VDM designation | LC-Nickel 99.2 |
| Applicable standards | | ASTM B160 | Bars | | ASTM B162 | Plates |
|
Chemical composition
| en % | Ni | Cu | Fe | Mn | C | Si | S | | min | 99,000 | - | - | - | - | - | - | | max | - | 0,250 | 0,400 | 0,350 | 0,020 | 0,350 | 0,010 |
Density : 8.89
Guarantee mechanical results in MPa
| Standard | Rm | Rp
0.2% | A % | Z | HB | Hrc | Comments | | ASTM B160 - 93 | 345 | 70 | 40 | - | - | - | Hot rolled, all sizes | | ASTM B160 - 93 | 345 | 70 | 40 | - | - | - | Annealed, all sizes |
Forging conditions
Forging is made at a range of temperature included between 1150 and 950°C, then cooled at appropriate conditions for the final thermal treatment and obtain required characteristics. In any case, please contact us.
Properties / Main use conditions
Same characteristics as 200. Its low carbon percentage makes it suitable for mentionned atmospheres but at temperatures over 300°C (570°F) due to a decreasing of the aptitudes for precipitation of hydrocarbons at the grain junctions.
Main applications
As the 200, hot caustic soda, production of soap, but its better ductility makes it more suitable for stamping or cold forging,
Heat treatment
Please, contact us
|