601
|  |
|
|
We propose this metal only as forged pieces, rings, blocks, bars, rolls (rough pieces, pre-machined, or machined as per your drawings).
|
| Carlier designation | NC23FeA |
| UNS designation | N06601 |
| European numbering designation | 2.4851 |
| AFNOR designation | NC23FeA |
| Thyssen Krupp VDM designation | Nicrofer 6023 |
Chemical composition
| en % | Ni | Cr | Fe | Mn | Al | C | Cu | Si | S | | min | 58,0 | 21,0 | Solde | - | 1,0 | - | - | - | - | | max | 63,0 | 25,0 | - | 1,0 | 1,7 | 0,10 | 1,0 | 0,5 | 0.015 |
Density : 8.1
Guarantee mechanical results in MPa
| Standard | Rm | Rp
0.2% | A % | Z | HB | Hrc | Comments | | ASTM B166 - 01 | 550 | 205 | 30 | - | - | - | All sizes, annealed |
Forging conditions
Forging is made at a range of temperature included between 1150 and 950°C, then cooled at appropriate conditions for the final thermal treatment and obtain required characteristics. In any case, please contact us.
Properties / Main use conditions
Refractory alloy, Ni-Cr-Fe with addition of Al, Ti and Zr, whichoffer a high resistance to oxidation until the temperature of 1100°C, together with good characteristics to creeping until 900°C.
Main applications
Industrial furnaces, heat treatment baskets, parts of glass ovens, chemistry and petrochemical industry.
Heat treatment
Please, contact us
|